Products Description

Pbat resin BF1113 is a modified PBAT raw material promoted by . With excellent processing properties, it is ideal for a variety of plastic bag applications. pbat resin BF1113 has 30% calcium carbonate, which improves the material's tensile strength, stiffness and other mechanical properties.

Properties	Test Method	Test Condition	Unit	Typical Values
Physicai
Density	ISO 1183-1：2004A	23℃	g/cm3	1.44
Melt Flow Rate	ISO 1133：2011	190℃,2.16kg	g/10min	3
Water Content		105℃	%	≤0.3
Ash Content	ISO 3451.1:2015	650℃,0.5h	%	30
Membranous(0.03mm)
Transverse Tensile Strength	GB/T 1040.3-2006	500mm/min	MPa	12
Transverse Elongation at Break	GB/T 1040.3-2006	500mm/min	%	400
Longitudinal Tensile Strength	GB/T 1040.3-2006	500mm/min	MPa	23
Longitudinal Elongation at Break	GB/T 1040.3-2006	500mm/min	%	200

Typical values are laboratory averages and are for reference only and are not to be considered as product standards.

Drying Condition
Drying Temperature			80℃
Drying Time			2h
Blow Molding Process
Blow temperature	region 1	region 2	region 3	region 4	region 5	Mold Head
	135	140	145	145	150	150
Maximum Blow Temperature			160℃

Note: The above blow details should be based on the shape of pruducts, mold design and injection molding machine specifications and other conditions vary,the specific shall be adjusted

Products advantage

One of the most notable features of Pbat Resin BF1113 is its excellent processing properties. It has a lower processing temperature and faster cooling rate compared to other similar materials, making the manufacturing process more efficient and cost-effective. The material also has good printability, which is essential for applications such as packaging materials.

Another critical advantage of Pbat Resin BF1113 is that it is environmentally friendly. PBAT is a bio-based material that breaks down in industrial composting facilities, making it an excellent choice for eco-friendly packaging materials. The addition of calcium carbonate also makes the material more durable, improving its resistance to tearing and puncturing.

Products application

The most common application for Pbat Resin BF1113 is in blown film production, used for products such as milk tea bags, garbage bags, and other similar products.

Biodegradable plastic bags

Biodegradable mulch

Why chooes us

Biodegradable plastic PBAT series products with independent intellectual property rights, leading domestic and
international product quality
2× 60000 ton synthesis unit and by-product THF recovery unit, with the largest single line production capacity in China Catalyst development ,trial, polit capability
Ability to develop catalysts and conduct small-scale and pilot tests

company information

Shandong Co., Ltd.

Shandong Co., Ltd. (referred as "", ) is a national high-tech enterprise specializing in the research and development, production, sales and service of high-performance thermoplastic elastomers, special rubber, modified plastics, functional masterbatches and color masterbatches. It has R&D innovation centers and production bases in Yantai Longkou, Qingdao, Beijing, Shanghai, Chongqing, and other places, the products include TPV, TPE, TPU, HNBR, modified plastics, meltblown materials, biodegradable materials, etc., which are widely used in automobiles, home appliances, new energy, E&E, rail transit, aerospace, medical health care, construction engineering and other fields.

large enterprise scale

Efficient and precise processing and testing equipment.

Standardized Production

Passed ISO9001 certification and obtained relevant patent certificates.

High-Quality Customized Services

Provide the pre-sale material selection, structural design, product matching, after-sales service one-stop solution.